| APPLICATION METHODS |
| |
RC-2000 can be applied by either brush, spray, or roller. Best results can be obtained with airless spray equipment.
The following table provides basic airless spray equipment information.
| Spray Equipment: | Airless |
| Orifice size: | 0.019-0.031 |
| Fluid Pressure (PSI): | 2500-3000 |
| Fluid hose size: | 3/8"-1/2" |
See Inland Application Bulletins for additional information.
|
| PRODUCT TEMPERATURE |
| |
For best spray application, the product should be at a minimum of 60° F. Lower temperatures can be utilized for brush applications.
|
| APPLICATION TEMPERATURE |
| |
For best results, the temperature of the ambient air and the substrate
should be within a range of 40°-110°F.
|
| SURFACE PREPARATION |
| |
The surface must be free of any moisture, rust scale or soil. Remove any
loose material from cracks or seams with a wire brush or scraper. Oil and
grease should also be removed. In many cases water blast will be sufficient
to prepare the surface.
|
| RC-2000 HANDLING & STORAGE |
| |
RC-2000 contains a blend of mild solvents which is considered
combustible by D.O.T. and O.S.H.A. standards. It should be used and
stored away from flames, in a well-ventilated atmosphere. Avoid prolonged
breathing of vapors and prevent contact with eyes. In case of eye contact,
flush with water for 15 minutes and call a physician. Read all label
information and precautions before using.
|
| RC-2000 TECHNICAL DETAILS |
| |
| Colors: | White/Gray/Beige |
| Type of Resin: | Synthetic Rubber |
| Coverage Rate: | 80-100 sq. ft/gal |
| Wet Mil Thickness: | 10-12 mils |
| Dry Mil Thickness: | 4-5 mils |
| Specific Gravity: | 1.02 |
| Weight: | 8.5 lb./gal. |
| Solids (% by Weight): | 49.0 ± 1% |
| Solids (% by Volume): | 36.0 ± 1% |
| Drying Time: | 1-3 hours |
| Reduction: | None |
| Flash Point: | 101° F. |
| Elongation (ASTM-D-412): | 500% |
| Tensile Strength (ASTM-D-412): | 1520 PSI |
Water Vapor Transmission
Permeance (ASTM-E-96): | 0.166 perms @ 10 mils |
|
The specifications, properties and performance of materials described herein are based on information believed to be reliable. Product specifications are subject to change without notice.